Brand Name : win-ceramic
Model Number : 0.4-3.0mm
Certification : SGS,DGM,ISO
Place of Origin : China
MOQ : 25kg
Price : $18-39/kg
Payment Terms : T/T, D/P, L/C, D/A, Western Union, MoneyGram
Packaging Details : 25kg/barrel, 1-1.25tons/pallet
Material : zirconia
ZrO2 : 80%
Density : 6.0g/cm3
Grain Size : 0.5μm
Wear Loss : <10ppm/hr(24h)
Fracture Toughness : 8.5 Mpam1-2
Crushing Load : 2000KN
Elastic Modulus : 200 GPA
Hardnesa : 9 Mohs
Thermal Conductivity : 3W/m.K
Cerium stabilized zirconia beads/ceramic media with good price
Application:
It is with the earth rare element “cerium”, so cerium stabilized zirconia bead has the biggest specific gravity in all zirconia beads series and it is very suitable for some special industries and grinding materials.
Especially for milling and dispersing high viscosity pastes and high purity products.
(1).Wear-resistant, corrosion-resistant products: paints, textiles, paints, printing and dyeing;
(2). High strength, high toughness products: magnetic materials, piezoelectric ceramics, dielectric ceramics ;
(3).To prevent pollution: medicine, food, cosmetics ;
(4).Ceramics: Electronic ceramics, refractory ceramics, structural ceramics.
Products Dimension
Ball
ø 0.4-0.6mm | ø 0.6-0.8mm | ø 0.6-0.8mm | ø 0.8-1.0mm | ø 1.0-1.2mm | ø 1.2-1.4mm |
ø 1.4-1.6mm | ø 1.6-1.8mm | ø 1.8-2.0mm | ø 2.0-2.2mm | ø 2.2-2.4mm | ø 2.4-2.6mm |
2.6-2.8mm | 2.8-3.0mm |
Composition | Wt% | 20% CeO2 + 80% ZrO2 |
Specific Density | g/cm3 | 6.0 |
Color | — | Yellow/Gold |
Bulk Density | g/cm3 | 3.85 |
Hardness | Mohs | 9 |
Elastic Modulus | GPA | 200 |
Thermal Conductivity | W/m.K | 3 |
Crushing Load | KN | ≥2000(ø2mm) |
Fracture Toughness | Mpam1-2 | 8.5 |
Thermal Expansion Coefficient | 10*10-6/℃(20-400) | 9.0 |
Wear Loss | ppm/hr | <10ppm/hr(24h) |
Grain Size | μm | ≤0.5 |
Features:
It has a gem-like hardness and density.Micro-structure of delicate, uniform, dense ceramics of the Quartet. Its excellent wear resistance and fracture toughness is particularly suited for grinding and dispersing high-solid-phase high-viscosity, high hardness of the paste.
(1).Long working life: 30 times longer life than glass beads, 6 times than zirconium silicate beads.
(2)High grindingefficiency: around 6 times than glass beads; 2 times than zirconium silicate bead
(3).Excellent wear resistance and fracture toughness.
![]() |